Abstract
The microstructural evolution and creep behavior of the Ti-43.5Al–4Nb–1Mo-0.1B alloy have been investigated by scanning electron microscope (SEM) and transmission electron microscope (TEM). The excellent creep property was obtained with a fully lamellar (FL) microstructure containing the least grain boundary βo phase (GB-βo). TEM results revealed that after creep testing the α2 →βo phase transformation was observed in the FL microstructure. The formation βo phase is associated with the accumulation of Mo element, which is confirmed by the energy-dispersive X-ray spectroscopy (EDS). Moreover, the formation of βo precipitation in α2 lamellae effectively decreased the generation of dislocations in (α2/γ) lamellae, thereby improving the creep resistance. For the near gamma (NG) microstructure of the as-forged sample, a large number of dislocations and dislocation tangles were observed in the globular γ phase (γ-glob), which are considered to be the dominant creep mechanism. Moreover, the ellipsoidal ωo phase was observed in the GB-βo phase, accompanying with dislocations and sub-boundaries formation. In sum, the excellent creep property of the β-solidifying γ-TiAl alloy is attributed to the fine FL structure with a small amount of GB-βo phase and the formation of βo precipitation in (α2/γ) lamellae.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Progress in Natural Science: Materials International
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.