The Influences of Addition of MgCO<sub>3</sub> on the Properties of the Magnesia Prepared Using Magnesite

Abstract

Micropowder MgCO3 was added into magnesite as raw materials to prepare magnesia using a two-step calcination method. The sample magnesite was characterized use X-ray diffraction (XRD) and scanning electron microscopy (SEM). Experimental results showed that the sample insulated at 1600° C for 3 hours before and after sintering presented a linear change rate of 15.6 % in the case of without adding micropowder MgCO3, the prepared magnesia had a bulk density of 2.31 g/cm3 and apparent porosity of 32.8 %, while MgO grain size was 3.11 μm. In the case of adding 8 % micropowder MgCO3, the sample magnesite before and after sintering showed a linear change rate of 17.9 %. The bulk density, apparent porosity of prepared magnesia were 2.46 g/cm3 and 28.1 % respectively, while the grain size of MgO was 5.15 mm.