Abstract
Carbon nanotubes/zirconia/hydroxyapatite biocomposites was prepared by hot-pressing sintering under Ar atmosphere. The influence of sintering temperature on the mechanical properties and microstructure of carbon nanotube/zirconia/hydroxyapatite biocomposites was studied. We tested the bending strength and fracture toughness by universal electronic materials testing machine. The component of the composites was tested by XRD. The fracture surface of the composites was observed by SEM. The results indicate that the bending strength and fracture toughness of the composites is lower when the sintering temperature is lower than 1200°C. The difference of bending strength and fracture toughness at 1200°C and 1300°C is little. The number of them has risen markedly than the low temperature which reached to189.2MPa and 1.8MPa·m-1/2 respectively. The composition of the composites is mainly of hydroxyapatite, zirconia, carbon nanotubes, and a small amount of calcium phosphate, which indicated that part of the hydroxyapatite has decomposed. SEM photographs show that the fracture surface of the composites sintered at 1200 °C and 1300 °C is ductile fracture status and has bigger density.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.