Abstract
Samples of 6 mol% Sc2O3 - 1 mol% CeO2 co-doped ZrO2 were fabricated by conventional ceramic processing methods and sintered at various temperatures from 1000 to 1650?C in air. The sintering conditions on microstructure and phase content are investigated using various characterization methods, including pycnometry, diffraction, and spectroscopy. The electrical conductivity of samples was investigated using electrochemical impedance spectroscopy (EIS). The effect of inductive load (measured from room temperature to 800?C) is discussed in low to high temperature regimes. At T<400?C since the arc is not a complete semicircle, the high-frequency arc could be fit using a constant phase element (CPE), while by subtraction of inductive load, a good fit is achieved using a capacitor element instead of CPE. The Arrhenius conductivity plot of samples reveals that the specimen sintered at 1600?C for 6 hours exhibits the highest conductivity. The activation energy (Ea) and conductivity preexponential (?0) factor are calculated from a linear fit to data that decreases by the increase in sintering temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.