Abstract
The number, and the spacing, of Ag3Sn precipitates in Sn-Ag-Cu/Cu solder joints were related to separate processing parameters. The mechanical properties of an individual solder joint were directly related to the resulting distribution of different dispersoids in the joint. As the number of Ag3Sn precipitates increased, so did solder joint strength and shear fatigue lifetime. The room-temperature shear fatigue lifetime was inversely correlated with the separation between Ag3Sn precipitates. Bi and Sb solid solution strengthening was found to result in significantly larger values of shear strength and shear fatigue lifetime for one Pb-free solder. Room-temperature shear fatigue lifetime tests were identified as a relatively straightforward, yet sensitive means to gain insight into the reliability of Sn-Ag-Cu (SAC) solder joints.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.