Abstract
Sol-gel zirconia films were deposited onto stainless steel and glass substrates by dip-coating. The correlation between the withdrawal speed, the sol composition and the resulting film thickness was studied. If a critical film thickness is exceeded, crack formation occurs. Cracking is one of the major drawbacks of the sol-gel deposition method because of the limitation of the maximum film thickness achievable without crack formation via single step deposition. The correlation between sol composition and crack formation was examined. Especially the role of polyethylene glycol (PEG)—an organic additive to reduce crack formation—was studied. Multi-layer coatings were deposited to characterize film density and hardness as a function of the heat treatment temperature from 400 to 800^∘C. The film density was found to be between 4 g cm−3 to 5.5 g cm−3 and the film hardness was in the range of 2.8 to 6.0 GPa, with a steep increase observed between 450 to 600^∘C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.