Abstract
The Young's modulus and flexural strength were determined for glass polyalkenoate cements as a function of poly(acrylic acid), PAA molar mass, concentration, glass volume fraction and cement ageing time. The Young's modulus was independent of PAA molar mass. The Young's modulus increased dramatically with the PAA concentration of the cement until concentrations greater than 50% m/m were reached. The modulus increased with time for nearly all the cements investigated consistent with a continuing ionic cross-linking process in the cement matrix. The modulus increased with an increase in the volume fraction of the higher modulus glass phase. Increasing the glass volume fraction provides more surface area for acid attack resulting in a more cross-linked polysalt matrix, as well as increasing the volume fraction of residual glass particles. Flexural strength was highly dependent on molar mass of the PAA and its concentration. The molar mass dependence of the flexural strength was greatest at higher PAA concentrations.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.