Abstract
The impact of heat input on mechanical aspects like joint strength, toughness, microhardness and metallurgical and corrosion characterization of UNS S31803 duplex stainless steel (DSS) in solid state continuous drive friction welding was studied. The experiments were carried out according to Design of Experiments (DOE) with L9 orthogonal array by varying the four different parameters namely friction pressure, friction time, upsetting pressure and upsetting time, keeping spindle speed as constant. Detailed analysis of fracture morphology, presence of elements and its distribution on joint zone were performed through scanning electron microscopy (SEM) attached with energy dispersive spectroscopy (EDS). No intermetallic phases were observed by X-ray diffraction (XRD) technique. Tensile strength results showed that higher the heat input the better was the preservation of joint strength. At room temperature, toughness decreased as heat input increased. At −100°C and −196°C, toughness of weld metal was comparatively higher than other fusion processes. Microhardness increased with an increase in heat input due to grain refinement. In addition, the corrosion behavior of the weld metal was also evaluated through potentio-dynamic polarization curve. Corrosion resistance of weld was better than that of base material and it is increased with an increase in the heat input.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.