Abstract
The growth kinetics of boride layer on boronized AISI 4140 steel is reported. Steel samples were boronized in molten borax, boric acid and ferro-silicon bath at 1123, 1173 and 1223 K for 2, 4, 6 and 8 h, respectively. The morphology and types of borides formed on the surface of AISI 4140 steel substrate were analyzed by means of optical microscopy, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS) and X-ray diffraction analysis (XRD). The boride layer thickness ranged from 38.4 to 225 μm. Iso-thickness diagrams for pre-determined thickness according to treatment time and temperature, were graphed by MATLAB 6.0 software. The hardness of borides formed on the samples changed between 1446 and 1739 HV 0.1, according to treatment time and temperature. Layer growth kinetics way analyzed by measuring the extent of penetration of FeB and Fe 2B sublayers as a function of treatment time and temperature in the range of 1123–1223 K. For practical use, an iso hardness diagram was established as a function of treatment time, temperature and boride layer thickness. The depth of the tips of the most deeply penetrated FeB and Fe 2B needles were taken as measures for diffusion in the growth directions. The kinetics of the reaction, K = K o exp ( - Q / RT ) were also determined by varying the treatment temperature and time. The results show that K increased with boronizing temperature. The activation energy ( Q) was formed to be 215 kJ mol −1. The growth rate constant ( K) ranged from 3×10 −9 to 2×10 −8 cm 2s −1.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.