The flow behavior and sealing ability of calcium silicate root canal cement containing dimethyl sulfoxide: An in vitro study

Abstract

IntroductionTo develop a calcium silicate (CaSi)-based cement containing dimethyl sulfoxide (DMSO) and cement deliver device for new root canal filling technique, and to assess the flow behavior, leakage, and root canal filling quality of CaSi containing DMSO. MethodsCaSi containing DMSO (CSC-DMSO) and CaSi containing PEG (CSC-PEG) were prepared, and the flow characteristics of both cements were compared in gypsum and resin channels using a high-speed camera. Eight root canals were obturated by CSC-DMSO or CSC-PEG using a cement delivery device, and root canal filling quality was assessed in terms of filling length using periapical radiographs. The filling length was evaluated by ‘apico-coronal extension,’ measuring length in reference to apical constriction. Microleakage was measured for thirty human molars that were randomly filled with CSC-DMSO, CSC-PEG, or gutta-percha and AH plus. Preliminary obturation of CSC-DMSO with cement delivery device in human teeth was analyzed in terms of filling length and void, using periapical radiographs. Statistical analysis was performed with the Kruskal Wallis test for simulated root canal fillings and one-way ANOVA for leakage test. ResultsThe flow speed of CSC-DMSO reduced in gypsum channels compared to resin channels, but CSC-PEG did not exhibit significant differences in the channels. The median absolute value of apico-coronal extension was significantly lower in CSC-DMSO compared to CSC-PEG (p < 0.05). Microleakage did not statistically differ between the groups (p > 0.05). In the preliminary obturation, the mean apico-coronal extension of CSC-DMSO was −0.297 ± 0.724 mm, while CSC-PEG was not feasible due to excess apical extrusions. ConclusionsCSC-DMSO could be considered as an alternative filling material for root canal obturation.