Abstract
Nanostructured two-dimensional (2D) WS2 reinforced Al-4Cu alloy matrix composites were prepared via spark plasma sintering (SPS) at 550 and 570 °C. The microstructure and interface characteristics of the composites were investigated. In situ formation of Al-W-Cu ternary phase at the grain boundaries of the Al-rich matrix phase was observed on sintering. High-resolution transmission electron microscopy (HRTEM) and scanning TEM (STEM) with quantitative mapping confirmed that the structure of ternary Al-W-Cu (Al12W0.6Cu0.4) belongs to bcc phase (space group: Im3̅ (204), similar to that of binary bcc-Al12W phase. Such bcc intermetallic phase was absent in pure Al-matrix under identical sintering conditions. The ternary intermetallic phase along with the retained 2D-WS2 contributed to about 41% increase in the hardness of the alloy composite. Nanoindentation hardness and Young’s modulus of the Al-W-Cu ternary intermetallic were found to be around 4.6 GPa and 104 GPa, respectively. The formation mechanism of Al-W-Cu intermetallic phase from 2D-WS2 nanosheets and Al-4Cu matrix was elucidated with Calphad (Calculation of Phase Diagrams)-based Gibbs energy analysis.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.