Abstract
In this work, hydroxyapatite (HA) powders were synthesized using calcium hydroxide Ca(OH)2 and orthophosphoric acid H3PO4 via wet chemical precipitation method in aqueous medium. Calcium‐to‐phosphorus (Ca/P) ratio was set to 1.57, 1.67, 1.87 that yield calcium‐deficient HA, stoichiometric HA, and calcium‐rich HA, respectively. These synthesized HA powders (having different Ca/P ratio) were characterized in terms of particle size and microstructural examination. Then, the densification and mechanical properties of the calcium‐deficient HA, stoichiometric HA, and calcium‐rich HA were evaluated from 1000 to 1350°C. Experimental results have shown that no decomposition of hydroxyapatite phase was observed for stoichiometric HA (Ca/P = 1.67) and calcium‐deficient HA (Ca/P = 1.57) despite sintered at high temperature of 1300°C. However, calcium oxide (CaO) was detected for calcium‐rich HA (Ca/P = 1.87) when samples sintered at the same temperature. The study revealed that the highest mechanical properties were found in stoichiometric HA samples sintered at 1100–1150°C, having relative density of ~99.8%, Young's modulus of ~120 GPa, Vickers hardness of ~7.23 GPa, and fracture toughness of ~1.22 MPam1/2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Applied Ceramic Technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.