Abstract
Turbines fired with hydrogen or syngas from coal gasification will have significantly higher water vapor contents in the combustion gas than natural gas fired turbines. The effect of increased water vapor on alumina-forming coatings and model alloys was investigated at 1100 °C in furnace cyclic testing. Increasing the water vapor content from 10% to 50 vol.% increased the amount of scale spallation on undoped alumina-forming alloys. Compared to dry O 2, increased spallation was observed for β and γ/γ' phase coatings on the substrates of alloys 142 and N5. In all cases, the addition of water vapor appeared to reduce the formation of alumina whiskers and ridges at the scale–gas interface, but did not significantly change the alumina growth rate. The addition of water vapor may have a detrimental effect on the selective oxidation of Al in γ/γ' alloys and coatings.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.