Abstract
In this work, Cu2SnS3 (CTS) films were prepared by a simple ultrasonic spray pyrolysis method on soda-lime glass substrates with different Cu/Sn precursor ratio and substrate temperature. The structural, component, morphological, optical and electrical properties of the films were investigated. XRD and Raman results confirmed that the Cu2SnS3 films were polymorphism with tetragonal phase and monoclinic phase. Sn-rich precursor and higher substrate temperature may change the dominant phase from tetragonal CTS phase to monoclinic CTS phase. Optical band gap of the films decreased from 1.87 to 1.03 eV with increasing Cu/Sn precursor ratio under 350 °C. All the films showed p-type conductivity with a minimum resistivity of 3.5 × 10−3 Ω cm. Additionally, the CTS films were annealed at 500 °C in sulfur atmosphere to improve the crystallinity and sulfur content. After annealing, a narrow band gap and pure CTS film was obtained, which could be a promising absorber layer material for high efficiency solar cell.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.