Abstract
In this paper, we investigate the effect of silica additive on the structural and luminescence properties of Eu3+ and Eu3+/Tb3+co-doped sodium-calcium phosphate glasses. Eu3+ doped phosphate glasses have been prepared using melt-quenching technique and characterized through X-ray diffraction (XRD), differential thermal analysis (DTA), Fourier Transform Infrared (FTIR), Raman spectroscopy, ultraviolet–visible (UV–Vis) and luminescence measurements at room temperature. The incorporation of SiO2 led to an increase of glass transition temperature (Tg), indicating an improvement of glass network rigidity. This result was correlated with FTIR and Raman investigations which revealed the occurrence of more hydration-resistant POSi bonds. An intense red luminescence has been observed due to 5D0 → 7F2 transition of Eu3+ ions in these glasses. The luminescence spectra for Eu3+/Tb3+ co-doped phosphate glasses were then recorded with various Eu3+:Tb3+ molar ratio. Dependence of luminescence lifetimes on the increase of Eu3+: Tb3+ molar ratio was investigated. It was observed that the energy transfer process occurs from Tb3+ to Eu3+ in the studied glasses. Our results show that a tuneable color is achieved when Eu3+: Tb3+ molar ratio changed. The variation of the excitation wavelength can also tune the luminescence spectra of the new phosphate glasses.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.