The Effect of NaOH Concentration and Curing Condition to the Strength and Shrinkage Performance of Recycled Geopolymer Concrete

Abstract

Concrete is widely used as a material construction. Globally, the consumption of concrete was estimated to be more than 8 billion tons per year. Nowadays, many problems arise related to concrete manufacturing occur especially on environmental issues. A key concern for environmentalists has always been climate change. One of the ways to mitigate the impact activities on the climate is to reduce carbon footprint. Portland cement are commonly been used in concrete is responsible for about 5% of all CO2emission. It is reported by Davidovit that the production of one ton of Portland cement emits approximately one ton of CO2into the atmosphere. There are several ways to reduce environmental pollution that cause by production and utilization of Portland cement, one of it is Geopolymer concrete. Subsequently Geopolymer concrete incorporating with recycle concrete aggregate (RCA) is one of the alternative to further reduce carbon footprint and as well as can reduce waste. Geopolymer concrete is a concrete that use no cement and produced by the combination of alkaline activator and supplementary cementitious material (SCM) such as fly ash, boiler ash, waste paper sludge ash (WPSA), ground granulated blast-furnace slag (GGBS), and so on in order to reduce carbon emission. In this study the Waste Paper Sludge Ash (WPSA) were used as a SCM and the combination of sodium hydroxide (NaOH) and sodium silicate (Na2SiO3) as a binder. Two (2) series of geopolymer concrete specimens comprising two (2) different molar of sodium hydroxide (NaOH) which are 8M and 14M were adopted. The effect variable alkaline molarity on the compressive strength and shrinkage of the geopolymer concrete specimens is tested at the age of 3, 7, 14 and 28 days. The mixture of geopolymer concete with 8M of sodium hydroxide (NaOH) concentration then was categorized into three (3) groups. Each group were been cured at different curing condition which are in ambient condition, oven, and external condition. The size of specimens prepared were 100mm x 100mm x100mm. The result shows that the molarities of sodium hydroxide (NaOH) influenced the strength of Waste Paper Sludge Ash (WPSA) based geopolymer concrete produced incorporating with increasing of recycle concrete aggregate (RCA). The result also show that the geopolymer concrete undergoes very low shrinkage. Curing condition will also effect the strength of geopolymer concrete produced.