Abstract
Micropowder injection molding (μPIM) is a new technology that has potential in the mass production of microcomponents. A bulk material of nanoparticles possesses completely different properties from those of large-sized particles. The main objective of this study is to study the effects of nano-sized powder addition on the μPIM process of powder-polymer mixtures for the fabrication of miniature parts. The binder systems consist of polyethylene glycol (PEG), polymethyl methacrylate (PMMA), and stearic acid (SA) with different powder loading blended with powders. The results indicate that increasing the nanopowder content to 30wt.% increased the powder loading and decreased the injection and sintering temperatures. The sintered parts had densities of 96% of the theoretical value. High physical and mechanical properties of the sintered specimen were achieved with the 30wt.% nano-sized powder sintered at 1200°C at a heating rate of 5°C/min under vacuum atmosphere. A significant reduction of the surface roughness of the sintered parts using the nano–microhybrid powder (Sa=0.365μm) was observed compared with the sintered parts with only micropowder (Sa=1.002μm). Using nanopowders, the hardness also increased from 182HV to 221HV with a linear shrinkage of approximately 9%, which is less than that of the micropowders (18%).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.