Abstract
Al-Ni hypoeutectic alloys were directionally solidified under upward transient heat flow conditions. The aim of the present study is to set up correlations between the as-cast microstructure and the resulting mechanical properties of these alloys. The dependence of primary and secondary dendrite arm spacing on the alloy solute content and on solidification thermal parameters is also analyzed. The results include transient metal/mold heat transfer coefficient, tip growth rate, cooling rate, dendrite arm spacing, ultimate tensile strength, yield tensile strength and elongation. Expressions relating dendrite spacing to solidification thermal parameters and mechanical properties to the scale of the dendritic microstructure have been determined. It was found that the ultimate tensile strength and the yield tensile strength increase with increasing alloy solute content and with decreasing primary and secondary dendrite arm spacing. In contrast, the elongation was found to be independent of both alloy composition and dendritic arrangement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.