Abstract
The thaumasite form of sulfate attack (TSA) has been observed in mortar prisms made from Portland–limestone cements after laboratory storage in 1.8% magnesium sulfate solution at 5 °C for 5 years. The prisms all showed evident signs of degradation, which increased with increasing limestone content. X-ray powder diffraction indicated that a solid solution was formed in all the prisms, which was based on the crystal structure of thaumasite, but extended towards the chemical composition of ettringite. The prism made from the cement with the highest level (35%) of limestone replacement gave the greatest amount of the thaumasite solid solution and had a composition close to the thaumasite end member, whereas those cements with lower (15%, 5% and 0%) levels of replacement gave reduced amounts of the solid solution and had greater lattice parameters. The solid solutions that have been observed are compared with those reported by Barnett et al. for synthetic thaumasite samples grown from sucrose solution.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.