Abstract
The effect of device fabrication temperature on the work function of ruthenium (Ru) metal gate and its bilayers was investigated. The work function shows strong temperature dependence when Ru electrodes are deposited on silicon oxide, SiO2, but not on hafnium silicates (HfSiOx). Specifically, the work function of Ru on SiO2 increased from 4.5 eV at 500 °C to 5.0 eV at 700 °C. On further annealing to 900 °C or higher, the work function dropped to about 4.4 eV. In the case of HfSiOx, the work function of Ru changed by less than 100 mV over the same temperature range. Identical temperature dependence was observed using hafnium (Hf)/Ru and tantalum (Ta)/Ru bilayers. However, the peak values of the work function decreased with increasing Hf/Ru and Ta/Ru thickness ratios. Materials analysis suggests that these trends are driven by interactions at the Ru metal gate–dielectric interface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.