Abstract
Ti–Al–Zr alloy has been oxidized at 360°C in alkaline steam at a pressure of 10.3 ± 0.7 MPa. Cross-sectional transmission electron microscopy (TEM) observations indicated that the oxide scale of Ti–Al–Zr alloy was composed of outer and inner subscales, in which the outer layer consists of anatase-TiO2 and the inner layer a mixture of TiO and Ti2O. The thickness of the Ti2O, TiO and anatase-TiO2 were approximately 50, 100 and 400 nm, respectively. These results were confirmed by X-ray energy dispersive spectrometry (EDS) measurements. The enhanced corrosion of titanium alloys in LiOH solution is attributed to a high hexagonal Ti2O to tetragonal TiO2 phase transformation rate induced by the substitution of Li+ for Ti4+ in the oxide layer.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.