Abstract
The bulk samples of milled and unmilled synthesized by conventional solid-state reaction. The powder X-ray diffraction and Rietveld refinement software program characterized crystal structure. The elementary mapping technique was used EDXS. For the onset critical temperature (Tconset) and offset critical temperature (Tcoffset) the four-probes measurement method was utilized. The superconducting compound and non-superconducting compound were incorporated in the samples. The Y123 was highest superconducting compound and lowest the non-superconducting compound. The c lattice parameter of milled samples was longer than unmilled samples. The anisotropy parameter of the milled samples had a lower value than the unmilled samples. The mapping technique showed that the without any impurity and composite of Y, Ba, Cu, and O. The critical temperature of milled, Y358, and Y7-11-18 were higher than unmilled. Conversely, the critical temperatures of milled and unmilled Y123 were closed to Y358 and Y7-11-18.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.