Abstract
The aim of research was developed area of nanoporous ceramic matrials of ternary - ZrO2-TiO2-SiO2 system. The ceramic materials of system ZrO2-TiO2-SiO2 was synthesized via sol-gel technology by hydrolysis of tetraethylorthosilicate (TEOS), zirconia propoxide and titanium isporopoxide solutions. The sols were polymerized at room temperature to obtain gels. Then gels were dried at 100 OC 72 hours. Xerogel was milled 1 or 6 hours and the powder was axial pressed for nanoporous ceramic samples. All the samples were sintered at 800 OC or 1000 OC in air. 1M HYPERLINK "res://\\\\ld1062.dll/type=1_word=hydrochloric%20acid" hydrochloric acid (HCl) and destilled water were used as a catalyst to promote the hydrolysis and condensation reactions. All samples were characterized by X-rays (XRD) diffraction, particle size distribution and compressive strength. Apparent density and specific surface area of ceramic samples were determined by a Brunauer, Emmett and Teller (BET) nitrogen adsorption-desorption isotherms.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.