Abstract
Durian-like gallium nitride (GaN) microstructures were successfully synthesized on Si substrate by pre-treating Ga metal with aqueous NH3 via catalyst assisted chemical vapor deposition (CVD) method at 1200°C. The as-synthesized product was characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX). XRD and EDX analysis revealed that durian-like GaN is pure and single phase. SEM results showed that the size of the durian-like GaN structures was 20–25μm. GaN microstructures exhibited reasonable field emission properties with the turn-on field of 8.24Vμm−1 (0.01mAcm−2) and threshold field of 10.18Vμm−1 (1mAcm−2) which is sufficient for applications of electron emission devices, field emission displays and vacuum micro-electronic devices. Photoluminescence (PL) properties of durian-like GaN studied at room temperature showed a strong near-band-edge emission at 369.4nm (3.36eV) whereas at low temperature it showed near-band-edge emission at 364.2nm (3.4eV) without yellow band emissions. The photoluminescence properties showed that it has also potential application in light-emitting devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.