Abstract
A well-defined fluorine-containing copolymer with pendant epoxy groups, poly(2,2,3,4,4,4-hexafluorobutyl methacrylate-block-glycidyl methacrylate) (PHFBMA-b-PGMA), was prepared by sequential atom transfer radical polymerization (ATRP). The amphiphilic copolymer PHFBMA-b-PGMA(OH) with pendant hydroxyl groups was obtained after ring-opening reaction of the epoxy groups from PGMA. The macroinitiator agent PHFBMA-Br and its copolymers were proved to be successfully synthesized by characterization of FTIR, 1H NMR and gel permeation chromatography (GPC). The chain growth experiment demonstrated that a linear first-order relationship was fitted under the conditions. In addition, the fluorinated copolymers with functional groups in the side chain could keep the contact angle and the advantages of fluoropolymers while improving the hydrophilic property. Meanwhile, TGA testing showed that the copolymers had better thermal stability than its homopolymer. TEM observation indicated that microspheres were embedded in the stable micelles when the final copolymer concentration of aqueous solution was 1wt%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.