Abstract
Yttrium-doped lithium manganese oxide (LiMn0.98Y0.02O2) was prepared by ion exchange of lithium for sodium in NaMn0.98Y0.02O2 precursors obtained by using rheological phase reaction method. This material had small particle size, which was composed of grain size of about 100 nm. Especially, LiMn0.98Y0.02O2 delivered the initial discharge capacity of about 191 mA h g−1 at room temperature when cycled between 2.0 and 4.4 V vs Li/Li+. Moreover, it showed an excellent cycling behavior, its specific capacity remained above 173 mA h g−1 after 20 cycles, and the material did not transform into spinel structure during the electrochemical cycling according to the cyclic voltammograms and X-ray powder diffraction. The electrochemical results revealed that the doping of Y3+ improved the performance of LiMnO2 considerably.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.