Abstract
The YBCO powder was prepared by oxalic acid precipitation method and consequent annealing. The correlation between pH values of oxalic acid solution and the precipitation percentage of precursors were analysed based on thermodynamics analysis. The differential scanning calorimetryanalysis (DSC) was used to confirm the synthetic technological parameter. The phases of powder in each process were investigated by XRD. The microstructures of each powder were tested by SEM and TEM. The mean grain size was calculated by the scherrer’s equation. The test results indicated that the YBCO powder with high purity, less impurities, smaller particle, but severe agglomeration, was Y123 when annealing at 900°C. However, adding dispersants could effectively solve the severe agglomeration. The size of YBCO particles was nanosized and coincided with the calculation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.