Synthesis and Comparison of Boron Nitride Nanostructure Prepared on Silicon and Molybdenum Substrates by Laser Plasma Deposition Technique

Abstract

ABSTRACTThe synthesis of boron nitride nanowires on silicon (Si) and nanorods on molybdenum (Mo) substrates at the same experimental conditions was composed. Fine tip nanowires with diameters around 50 nm were produced on Si substrates, whereas, nanorods with diameter around 100 nm were formed on Mo substrates. The change in length from 5 μm to 100 μm for nanowires and 0.2 μm to 0.8μm for nanorods following variation of substrate temperature were studied systematically.Scanning Electron Microscopy was used to analyze the surface images of BN nanowires and nanorods. Energy Dispersive X-Ray spectroscopy (EDS) was used to analyze boron and nitrogen concentration in the samples. The crystal structures of BN samples were investigated using Raman spectroscopy and x-ray diffraction. The experimental results showed that the nanorods are hexagonal mixed with cubic, whereas the nanowires are hexagonal.