Abstract
AbstractA new class of materials based on inorganic and organic species combined at a nanoscale level has received large attention recently. In this work the idea of producing hybrid materials with controllable properties is applied to obtain foams to be used as catalyst supporting. Hybrids were synthesized by reacting poly(vinyl alcohol) in acidic solution with water glass. The inorganic phase was also modified by incorporating a hexamethyldisiloxane as precursor. The hybrid aerogel powder was analyzed by scanning electron microscopy, TG‐DTA, Nitrogen adsorption–desorption, X‐ray diffraction and fourier transform infrared spectroscopy (FTIR) spectroscopy. The powder obtained had a higher porosity varying from 65 to 90% and the nanopore diameter ranged from 17 to 20 nm. The surface area and nanopore volume decreased as polymer content increased in the hybrids. The sharp decline in the weight observed at around 500°C accompanied an exothermic peak of the DTA curve. The sharp peak was observed around 211°C represents the DTA curve of Poly vinyl alcohol constituent in nano hybrids. The peak at 1638 cm−1 in the FTIR indicated the formation of SiOPVAOSi bridge in aerogel powder. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.