Abstract
Platinum (Pt) catalyst and nitrogen-containing silane (NS) were introduced to improve the thermal stability of silicone rubber. The effects of Pt and NS on thermal stability and degradation mechanism of silicone rubber were investigated by thermogravimetry (TG), thermogravimetry-Fourier transform infrared spectrometry (TG-FTIR), scanning electron microscope-energy dispersive X-ray spectroscopy (SEM-EDXS) and Fourier transform infrared spectrometry (FTIR). A significant synergism was found between Pt and NS for improving the thermal stability of silicone rubber. When 6.67ppm of Pt and 1.4 phr of NS were introduced, the temperature of 10% and 20% weight loss under nitrogen atmosphere were respectively increased by 36°C and 119°C. Meanwhile, the residue weight at 900°C was doubled to 68% in the presence of Pt/NS. The synergistic mechanism might be that the nitrogen atom coordinated with Pt and improved the catalytic efficiency of Pt. Additionally, NS preserved the catalytic activity of Pt under air atmosphere. Hence, Pt/NS efficiently catalyzed thermal crosslinking and suppressed degradation of silicone chains. Moreover, it revealed that the presence of Pt/NS protected silicone chains from oxidation. Thus, the unzipping depolymerization by silanol groups was reduced significantly.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.