Abstract
The surface microhardness and flexural strength of colored zirconia were examined. Two groups of zirconia disks (1mm thick, 20mm in diameter) within 5 disks each were shading with the same coloring liquids IL2 (Vita Classic-scale) when another group of 5 disks measured in no color. The shading time of one group was 3s and that of the other group was prolonged to 30s. The mechanical properties were tested after sintering at 1500°C. Data were evaluated using ANOVA analysis. Disks of shading 30s showed a lower strength 712 53 MPa. The value of 3s was 853 46 MPa. There were no significant difference on microhardness between the two shading time. Prolonged the shading time lowered the biaxial flexural strength of zirconia ceramic, but shading time did no effect on surface microhardness.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.