Abstract
Crystalline silicon kept at atmospheric pressure was irradiated with 775 nm multiple laser pulses of 150 fs duration at repetition rate 250 Hz. The laser pulses were circularly polarized, with a peak laser fluence of 0.03 J/cm2. We observed surface damage at a much lower fluence and lower number of pulses compared to that reported in the literature. Surface damage, cracks and pits formation were observed. The evolution of the surface damage as a function of the number of laser pulses was recorded. The observations were in contrast to the findings in the literature that the silicon surface became structured when irradiated by multiple pulses.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.