Abstract
Artificial hip joints are generally expected to fail due to wear after approximately 15years and then have to be replaced by revision surgery. If articular cartilage can be integrated onto the articular surfaces of artificial joints in the same way as osseo-integration of titanium dental implants, the wear of joint implants may be reduced or prevented. However, very few studies have focused on the relationship between Ti surface and cartilage. To explore the possibility of cartilaginous-integration, we fabricated chemically treated Ti surfaces with H2O2/HCl, collagen type II and SBF, respectively. Then, we evaluated surface characteristics of the prepared Ti samples and assessed the cartilage formation by culturing chondrocytes on the Ti samples. When oxidized Ti was immersed in SBF for 7days, apatite was formed on the Ti surface. The surface characteristics of Ti indicated that the wettability was increased by all chemical treatments compared to untreated Ti, and that H2O2/HCl treated surface had significantly higher roughness compared to the other three groups. Chondrocytes produced significantly more cartilage matrix on all chemically treated Ti surfaces compared to untreated Ti. Thus, to realize cartilaginous-integration and to prevent wear of the implants in joints, application of bioactive Ti formed by chemical treatment would be a promising and effective strategy to improve durability of joint replacement.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.