Abstract
In this work, poly(hydroxybutyrate-co-hydroxyhexanoate) (PHBHHx) film was fabricated by a solution-casting method and subsequently was modified by NaOH treatment to improve the surface hydrophilic property. Surface properties including hydrophilicity, surface appearance and functional groups were characterized by water contact angle measurement, scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The results showed the hydrophilicity of PHBHHx film was obviously improved by the NaOH treatment due to the topography changes promoted by the NaOH-etching and the introduction of polar groups included hydroxyl and carboxyl on the topmost surface layers. However, the modified film exhibited an aging effect: the hydrophilicity decreases with time elapsed during storage. It was found that the aging rate was strongly dependent on the crystallinity of the film and the storage environment. The sample with high-crystallinity lost hydrophilic property slower than that with low-crystallinity. Hydrophilic and low-temperature environment also prevented the modified PHBHHx from fast losing of the hydrophilicity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.