Abstract
WBe2, which occurs in space group 194, with hexagonal symmetry P63/mmc, is prepared by arc-melting at temperatures above 2200 C, where Be vapor loss is significant. This study is motivated by recent work on MoB2 and WB2, both superconductors (Tc=32 and 17 K respectively) under high (∼70 GPa) pressure. In order to avoid the known Be-rich superconducting phases (WBe13 and WBe22) in the complex phase diagram, both known to be superconducting at 4.1 K, the sample was prepared with a slight (∼5 %) excess of W. The resultant sample, prepared using high purity (99.999 %) Be, is essentially single phase WBe2, with some spread in its superconducting properties due to the known homogeneity range. (WBe2 forms in space group 194 between approximately W1.02Be1.98 and W0.88Be2.12.) Characterization was carried out with x-ray diffraction, electrical resistivity, ρ, in zero and applied magnetic fields, and specific heat. The resistivity in zero and applied fields and specific heat data indicate that our sample of WBe2 is a bulk superconductor at ambient pressure with a Tconset in ρ at 1.05 K, and Tc(ρ→0) at ∼0.86 K. There is no signature of superconductivity in ρ at 4.1 K, indicating successful avoidance of WBe13 and WBe22. The ρ data in field indicate an upper critical field of approximately 400 gauss.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.