Abstract
AbstractRecently, the natural fibers‐reinforced composites have attracted substantial attention as a potential structural material for low cost applications. The composites of poly(lactic acid) (PLA) with three kinds of natural fibers, such as bamboo fibers, wood fibers, and coconut fibers (CTFs), were prepared by solution‐casting technique. The natural fibers were modified by aluminum acid ester coupling agent and stearic acid to improve compatibility. To compare the mechanical and thermal properties of composites, tensile test, dynamic mechanical analysis, differential scan calorimeter, scanning electron microscopy (SEM), and Vicat softening point test were carried. The results showed that the addition of three kinds of natural fibers all could improve the mechanical and thermal properties of composites, and natural fibers after modification could further improve tensile strength of composites. And in comparison, the composite of PLA/CTF had highest tensile strength and best thermal properties. When the content of natural fibers were 2%, the highest tensile strength of PLA/modified CTF composites was highest, and it reached 22.5 Mpa which was 20.4% higher than that of pure PLA, and VST of this composite increased compared with pure PLA. Meanwhile, the results of SEM indicated that the modified CTF had best interfacial compatibility to PLA. These results indicated that PLA/natural fiber composites had higher strength and better heat resistance than pure PLA. This study provided the application of PLA industry with a feasible method. © 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.