Abstract
AbstractLocalized corrosion morphologies of 2195 Al‐Li alloy with various heat treatment in 4.0% NaCl solution (pH 6.5) were investigated, and its corrosion mechanism was studied using a three‐electrode coupling system of α (Al) substituting for the precipitate‐free zone (PFZ), simulated bulk θ′ (Al2Cu) and T1 (Al2CuLi). θ′ acts as cathodic zone in the alloy. At the initial stage, T1 phase is active with respect to θ′ and α (Al), and endures the main anodic current, indicating that anodic dissolution occurs on T1. However, its potential moves to positive direction with immersion time, due to dealloying of Li from T1. As a result, the main anodic dissolution occurs on α (Al) at a later stage. At this stage, as only T1 and α (Al) are coupled, T1 is cathodic to α (Al). In real 2195 alloy, T1 phase is very tiny, and anodic dissolution of T1 and PFZ occurs alternately. These results show that its intergranular corrosion or intersubgranular corrosion is caused by alternate anodic dissolution of T1 phase and PFZ along grain and subgrain boundaries.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.