Abstract
This study investigated the effect of intermediate annealing (IA) during a special thermo-mechanical treatment on the microstructure and properties of 7185 Al alloy. The results show that after IA, many sub-structures are formed in the alloy and many particles are precipitated. The particle size increases and the width of the dislocation wall becomes narrower with increasing IA time and temperature. After the second stage of deformation, the dislocations are ordered again and generate micro shear bands (MSBs). The final T6 treated alloy under IA2 process (holding time for 40 min at 400 °C) has good plasticity and corrosion resistance. The tensile strength is 523 MPa, the yield strength is 458 MPa, the elongation is 17.6%, the depth of intergranular corrosion layer is 15.6 μm, and the corrosion grade after 6 and 12 h exfoliation corrosion is N, PC.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.