Abstract
In this paper, aluminum coatings were prepared on a steel substrate by thermal spraying, and the corrosion morphology and corrosion resistance of the coating were investigated by salt spray and immersion tests. The results showed that after three months of salt spray tests, the coating still exhibited a surface morphology without significant damage and had good damage tolerance. Further effective protection of the substrate can be achieved by spraying the coating surface with paint. After three months of immersion test, the corrosion rate of samples with thicker coatings was located between 0.002 mm/y and 0.005 mm/y, and only a small amount of corrosion products was observed on the coating surface. The coated samples after salt spray and immersion tests maintained sufficient adhesion (17.07 MPa and 19.25 MPa), and the surface aluminum coating was highly reliable for protection of the steel substrate. In general, the reliability of the coating can be further improved by painting the surface of the thicker Al coating. This provides more ideas for the protection of transmission and transformation equipment.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.