Abstract
The bulk amorphous FINEMET was prepared from ribbon and powder by shock wave compaction. The magnetization of compacts was measured up to 550/spl deg/C. The Curie and crystallization temperature was 350/spl deg/C and 495/spl deg/C respectively. From the magnetization curves of as-compacted and annealed samples measured at room temperature in the external magnetic field up to 1.8 T, the effective anisotropy and the law of approach to saturation was derived The deviation from saturation was ascribed to the stress related structural defects in ribbon compacts with prevailing effect of the point-like defects. In the powder compacts the deviation was caused by the intrinsic magnetostatic fluctuations due to spatial inhomogeneity. >
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.