Abstract
The degradation of diffused SiC PIN diodes during forward-biased operation was studied by first fabricating PIN diodes by diffusion of aluminum or boron into 4H-SiC substrates with n-type 10-15 µm thick epilayers doped by nitrogen up to 5x1015cm-3. The formed diodes were subjected to degradation testing under an applied current density of 200A/cm2 at room temperature. The majority of the Al diffused diodes demonstrated a voltage drift, ΔVf, of more than 2 V, while B-doped diodes showed no significant change in forward voltage. The EBIC mode of SEM was employed to monitor nucleation and expansion of stacking faults.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.