Abstract
We report the structure and transport properties of current-perpendicular-to-plane spin valves (CPP SVs) with Co2FeAl0.5Si0.5 (CFAS) or Co2MnSi (CMS) Heusler alloy magnetic layers and an Ag or Cu spacer layer. A multilayer stack of sub/Cr/Ag/Heusler/(Ag or Cu)/ Heusler/Co75Fe25/Ir22Mn78/Ru was deposited on a MgO(001) single crystalline substrate by magnetron sputtering. Transmission electron microscopy observations showed epitaxial growth from the substrate to the top Heusler layer. The CPP SV with a CFAS/Ag/CFAS trilayer showed relatively large magnetoresistance (MR) ratios of 12% at room temperature and 31% at 12 K, with monotonous temperature dependence. However, the MR values of the SV with the CMS/Ag/CMS trilayer showed a different temperature dependence with a maximum value of 22% at 100 K. This might be related to the 90° couplings between the two CMS layers.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.