Abstract
The two-staged thermoelastic martensitic transformation (TMT) B2→R→B19′ in polycrystalline equiatomic NiTi has been studied by means of measurements of strain amplitude-independent and amplitude-dependent internal friction (ADIF), Young’s modulus and amplitude-dependent modulus defects. The internal friction measurements were performed at a frequency of about 100 kHz, rendering negligible the transient internal friction component and allowing one to investigate the structural internal friction, much less dependent on the external parameters such as the heating/cooling rate or the frequency of vibrations. Attention is focussed on the amplitude-dependent anelasticity. Based on the data obtained, the anelasticity is associated with the dislocations inside the martensitic variants, not with the interfaces or interface dislocations, as is traditionally done. The ADIF and anelastic strain in the R phase have been found to be an order of magnitude higher than in the B19′ martensitic phase. This observation is explained by a much higher density of the dislocations inside the variants of the R phase as compared with that of the B19′ phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.