Abstract
The influence of substrate temperature and nozzle-to-substrate distance (NSD) on the structural, morphological, optical and electrical properties of Sb:SnO2 thin films prepared by chemical spray pyrolysis has been analyzed. The structural, morphological, optical and electrical properties were characterized by using XRD, SEM, UV-visible spectrophotometry and Hall effect measurement techniques. It was seen that the films are polycrystalline, having a tetragonal crystal structure with strong orientation along the (200) reflection. The pyramidal crystallites formed due to coalescence were observed from SEM images. The values of highest conductivity, optical transmittance and figure of merit of about 1449(Ω·cm)−1, 70 %and 5.2 × 10−3 □/Ω, respectively, were observed for a typical film deposited using optimal conditions (substrate temperature = 500 °C and NSD = 30 cm).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.