Abstract
An exhaustive study of structural, dielectric and impedance analysis on Pr0.6Sr0.4Mn1−xTixO3±δ (0⩽x⩽0.4) perovskites were performed. Polycrystalline samples were prepared using solid state reaction method. The crystallographic structure was studied by X-ray diffraction experiments and Rietveld refinement revealed that all samples crystallize in an orthorhombic structure with Pnma space group. The approximate grain size was found from experiments’ scanning electron microscopy. The electrical response was studied using the impedance spectroscopy technique over a broad frequency range (0.1Hz–1MHz). The values of total conductivity for all samples were well fitted by the Jonscher law σtot(ω)=σdc+Aωn. For 0⩽x⩽0.3 samples, the hopping process occurs through long distance, whereas for x=0.4 compound the hopping occurs between neighboring sites. The Pr0.6Sr0.4Mn0.6Ti0.4O3±δ sample presents the lowest real part Z′ and the highest dc-conductivity σdc among these samples. For x=0.3 and 0.4 compounds, the variation of the imaginary part Z′′ shows a peak at a relaxation frequency related to the relaxation time (τ) by τ=1/2πfr. Nyquist plots of impedance show semicircle arcs for samples beyond 20% Ti content and an electrical equivalent circuit has been proposed to explain the impedance results.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.