Abstract
In this work, the results of the study on the optical properties of the perovskite structure ABO3 with La 3+ substitution for ions K + and Na + in the A site and Ti 4+ substitution for ion Nb 5+ in the B site are presented. The ceramics were sintered at 1100 ℃ and 1190 ℃ and formed at 10 MPa and 80 MPa. Dense ceramics were obtained with 94% of the theoretical density. The piezoresponse force microscopy (PFM) showed needle-shaped grains with a size of 30 nm for the samples formed at 10 MPa at both sintering temperatures. Apparently, the high temperature and high pressure used in formation reduced the energy of the band gap (Eg) from 3.36 to 3.09 eV. Strong emissions to 2.19, 1.86, 2.5, and 2.31 eV were obtained by exciting the samples at 325, 373, 457, and 500 nm, respectively; these emissions corresponded to blue-yellow-red regions of the visible spectrum.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.