Abstract
Magnetic fine particles of cobalt ferrite (CoFe 2O 4) have been synthesized using complexometric method in which ethylene diamine tetra acetic acid C 10H 16N 2O 8 (EDTA) acts as a complexing agent. The crystallographic structure, microstructure and magnetic properties of the synthesized powder were characterized by using X-ray diffraction (XRD), particle size analysis and vibrating sample magnetometry (VSM). The material crystallized in cubic spinel structure with lattice parameter of about 8.38 Å. Depending on the calcining temperature, the particle size of the powders varies in the range of hundreds of nanometers to tens of micrometers. A desired relative density above 95% of the theoretical value is obtained for the bulk sample after sintering. The calcined powders and sintered sample exhibit saturation magnetizations around 80 Am 2/kg which is expected for inverse CoFe 2O 4. With increasing calcining temperature the coercivity of these samples decreases. This simple synthesis route leads to a reproducible and stoichiometric material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.