Abstract
Controlling the morphology, composition, and crystalline phase of mesoporous nonnoble metal catalysts is essential for improving their performance. Herein, well-defined P- and B-codoped NiFe alloy mesoporous nanospheres (NiFeB-P MNs) with an adjustable Ni/Fe ratio and large mesopores (11nm) are synthesized via soft-template-based chemical reduction and a subsequent phosphine-vapor-based phosphidation process. Earth-abundant NiFe-based materials are considered promising electrocatalysts for the oxygen evolution reaction (OER) because of their low cost and high intrinsic catalytic activity. The resulting NiFeB-P MNs exhibit a low OER overpotential of 252mV at 10mA cm-2 , which is significantly smaller than that of B-doped NiFe MNs (274mV) and commercial RuO2 (269mV) in alkaline electrolytes. Thus, this work highlights the practicality of designing mesoporous nonnoble metal structures and the importance of incorporating P in metallic-B-based alloys to modify their electronic structure for enhancing their intrinsic activity.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.