Abstract
We report the optical properties of CdSe quantum dots (QDs) synthesized under various growth conditions, such as growth temperature, growth time, ligand ratio, and Cd:Se ratio of the precursors. As the growth temperature and time was increased, the peaks of the photoluminescence (PL) spectra were a red shifted, indicating that the size of QDs increased. Different ligand ratios and Cd:Se ratios of the precursors played important roles in determining the QDs size. From the PL spectra and the transmission electron microscopy image, the size distribution, as well as the size of CdSe QDs, could be controlled by using the growth conditions. The temperature-dependent PL of CdSe QDs dropped and dried on Si substrates was measured at temperatures from 15 K to 290 K. With increasing temperature, the red shift of the QDs was about 35 meV, which is noticeably smaller than that of bulk CdSe (∼100 meV). The influence of the temperature on the optical properties of colloidal CdSe QDs is important for an application to various devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.