Size effect on thermoelectric properties of Bi2Te3 nanoparticles

Abstract

Bi2Te3 nanoparticles exhibit size dependent thermoelectric properties which gives an opportunity to tune the size for optimization of the thermoelectric figure of merit (ZT). We have quantitatively analyzed the thermoelectric properties of Bi2Te3 using phonon scattering mechanism by incorporating the scattering of phonons with defects, grain boundaries, electrons and Umklapp phonon scatterings. The maximum value of ZT = 0.92 is obtained at T = 400 K for 30 nm Bi2Te3 nanoparticles in comparison to ZT = 0.45 for 150 nm nanoparticles at the same temperature. With decrease in size of nanoparticles interface volume ratio increases which increase the phonon scatterings with grain boundaries and point defects, results in decrease in thermal conductivity due to reduction in mean free path of phonons. As a result of decrease in thermal conductivity (κ), Seeback coefficient (S) and ZT increases.Bi2Te3 nanoparticles exhibit size dependent thermoelectric properties which gives an opportunity to tune the size for optimization of the thermoelectric figure of merit (ZT). We have quantitatively analyzed the thermoelectric properties of Bi2Te3 using phonon scattering mechanism by incorporating the scattering of phonons with defects, grain boundaries, electrons and Umklapp phonon scatterings. The maximum value of ZT = 0.92 is obtained at T = 400 K for 30 nm Bi2Te3 nanoparticles in comparison to ZT = 0.45 for 150 nm nanoparticles at the same temperature. With decrease in size of nanoparticles interface volume ratio increases which increase the phonon scatterings with grain boundaries and point defects, results in decrease in thermal conductivity due to reduction in mean free path of phonons. As a result of decrease in thermal conductivity (κ), Seeback coefficient (S) and ZT increases.